MatriCS consists of an St2LG (A366) steel core 0.25 mm thick with a fiberreinforced, high- grade NBR elastomer coating with a thickness of 0.125 mm applied to both sides.
MatriCS plusdiffers from MatriCS in that the core material is springy stainless steel 1.4310 (301) with a thickness of 0.2 mm, and the elastomer coating is somewhat thicker (approx. 0.15 mm).
Weight per surface unit
MatriCS kg/ m² ≈ 2.20
MatriCS plus kg/ m² ≈ 1.80
Stress resistance acc. to DIN 52 913
16 h, 300 °C N/ mm² > 45
Compressibility and recovery
acc. to ASTM F 36, procedure J
compressibility % 4 - 10
recovery % > 40
Short- term peak temperature °C 300
Operating temperature °C -40 up to +220
Installed surface pressure
max., at 220 °C N/ mm² 100